Hot wire is made of high quality low carbon steel, high carbon steel, after drawing, hot galvanized processing galvanized wire. Hot dip galvanized wire production process: wire rod – drawing – annealing – drawing – annealing – galvanized. Hot dip galvanized wire has the characteristics of thick coating, strong corrosion resistance and solid coating. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire. Hot-dip galvanized wire is of better quality than electrodip galvanized wire. In the production process, hot dip galvanized wire has more than one annealing process, so the corrosion resistance of hot dip galvanized wire is stronger than that of electric galvanized wire.

Remind you to buy galvanized iron wire, should be stored in dry, good ventilation conditions, do not contain corrosive gases, do not mix with the production of organic volatile gas paint, plastic and other substances in a good environment. If conditions, for galvanized parts to increase reliable inner packaging, and put desiccant. If the zinc layer white spots and hair, only mechanical removal, and then normal passivation, or thoroughly washed off the zinc layer after re-plating.

Summer is the breeding season of mosquitoes, at this time, not only should pay attention to pet food and drinking water clean, but also pay attention to cleaning the dog cage regularly, so as to avoid pet disease.

When this ore is specially refined into metallic iron, carbon, silicon, manganese, and other elements are added to it, so that the refined material is called general pig iron, which is also the material for the initial grade. According to the different requirements of the industry, different weights of alloy ingots are prepared in the smelting furnace according to the standard, such as weaving, Ming, paper, Lang, silicon, etc., and this smelting material is called combined gold ore.

Electric galvanized shaft wire direct selling is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.

The large roll of galvanized wire is like the literal meaning, is wrapped in a layer of zinc on the surface of low carbon steel wire material, beautify the appearance at the same time, but also improve the corrosion resistance of galvanized wire. Zinc dissolves easily in acids and also in bases, so it is called a bi-soluble metal. Zinc changes little in dry air. In moist air, a dense basic zinc carbonate film forms on the surface of zinc.

Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

Breeding cattle and sheep with barbed rope effect or better, because the advantages of barbed rope more. Then the barbed rope used for animal husbandry effect is good?

Want to keep a dog friends need to know: choose suitable dog and family environment of the cage, the dog cage to consider the material, the size of the dog, space, location, whether easy to clean and so on. Let’s take a look at these aspects.