Post time: 12-04-23According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing molding, pickling rust removal, high temperature annealing, hot galvanized, cooling and other processes. The following points should be paid attention to in the use of galvanized iron wire:
Post time: 10-03-23- Because of the pre-tension given to the packaging and binding of galvanized wire, it has the excellent characteristics of low relaxation value, small stress loss, good stability after loading, not easy to deformation, no fracture, strong elasticity, ordinary steel lines and rebar are difficult to compare. The use of advanced galvanized finishing process, therefore, the use of hot-dip galvanized steel wire construction, not only good corrosion resistance, but also beautiful and generous. The product has the characteristics of smooth surface, high dimensional accuracy, good uniformity of zinc layer and strong adhesion.
Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.
- D, coating adhesion; The zinc layer of the plating parts should be firmly combined with the base metal with sufficient adhesion strength, and will not fall off or bulge after the hammer test.
The amount of zinc on the surface of high zinc barbed rope is about 5 times that of general zinc barbed rope, thus greatly prolonging the time of rust resistance. In the appearance of the two products are silver white and metal texture is better, for the distinction between the two products is more difficult to distinguish if it is a layman, but for long-term work of professionals can be separated from the two at a glance.
Post time: 26-09-22Most of the production enterprises or large public places, they can play a defense hook mesh in the choice of time, often will hook mesh quality in position, so galvanized hook mesh this product few people are interested in, but does this show that galvanized hook mesh is not useful?
- Galvanizing can be done by zincate galvanizing or chloride galvanizing. Appropriate additives should be used to obtain a coating that meets the requirements of this standard. Light treatment should be carried out after light plating. The parts that need to be dehydrogenated for passivation should be passivated after dehydrogenation. Before passivation, 1%H2SO4 or 1% hydrochloric acid should be applied for activation for 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.
Post time: 13-12-22- In fact, although galvanized hook net is a useful material for iron products, but fundamentally speaking, modern hook net through continuous transformation and improvement, even if it seems to be not useful products, also have a role in its use, here we can turn our attention to people abandoned galvanized hook net.
Generally, galvanized wire used for welding is required to have a certain hardness. After acceptance of galvanized wire, the first thing to do is to feel the hand, and the other thing is to test on the machine. Because the average user does not have testing equipment, it is also very inconvenient to test on the machine. Use a micrometer to measure the diameter of galvanized wire evenly, and keep it about 0.02mm above and below the contract signing standard, with neat appearance, no leakage plating and no mess.
- 2. Drying: Dry the washed steel wire through hot air or other drying equipment to remove water.
Post time: 18-04-23Cleaning and disinfection methods of pet dog cage:
Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
- The chromium-plated layer has good thermal property. When the temperature is heated below 500℃, its luster and hardness are not changed obviously. When the temperature is higher than 500℃, the initial oxidation and discoloration occur, and the hardness decreases when the temperature is higher than 700℃. The friction coefficient of chrome coating is small, especially the dry friction coefficient, which is low among all metals. So the chrome coating has good wear.
- Reverse twisting of the barbed rope: first wrap the barbed wire around the main wire (that is, a single piece of iron wire) and then add an iron wire and twist together to form a double strand of barbed rope.
Ordinary blades installed on the walls of the barbed wire fence height in two metres of general construction cost in more than a dozen yuan a metre, but if the prison on the height of the wall construction modest have already reached the four or five meters so that every one meter of the cost of construction in 30-40 yuan, mainly because the work high above the risk is bigger. The construction cost is different, but the price of the blade barbed rope is the same. The construction cost is often higher than the product. In this way, the blade barbed rope factory recommends customers to use the blade barbed rope with better quality to avoid the tedious time and cost of subsequent removal and installation.