This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need yo have a variety of conditions, will need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer in the data does not fit the strength requirements, after all, there is no way to make the strength of the product progress, so this is the condition to.

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Large volume galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 grams/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, silk screen preparation, highway guardrail, product packaging and daily civil and other fields. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire).