Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

For the barbed rope products produced by the barbed rope factory, the number of rotating turns between the two thorns is usually 3-5. What is the internal relationship between this and the length of use?

Before wall plastering, the wall column is connected to the gap construction wire mesh, which can play a certain strengthening and heat preservation effect. The mesh is hung on the interface surface of different grassroots, and the length of each side should meet the requirements of 100mm, so as to prevent shrinkage and cracking caused by different grassroots. Mesh wire diameter can also determine the effect and efficiency of construction, mesh fine laid up convenient soft, high construction efficiency; Of national standard can assure quality, but laid respect is inferior to fine construction fast.

Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.