Stainless steel barbed rope in the way of corrosion is not very, because the surface is not treated but rely on its own raw materials for corrosion resistance, so there will be no chemical reaction. After a long time of use, it will not rust like the corrosion layer on the surface of hot dip galvanized barbed rope, because the internal material of stainless steel barbed rope is the same as the material on the surface. The most obvious difference in a short time is the cross section of this piece, hot dip galvanized barbed wire because of surface anticorrosion treatment, so there will be rust in the cross section of this piece, and stainless steel barbed wire because the internal raw materials and surface raw materials are consistent, so there is no such situation.

The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.

With the increasingly extensive use of hook mesh, the method of bridge rail is also different. The height of sidewalks or seatbelt outer railings should not be lower than 1.10 metres. The net distance between railings should not be greater than 140 mm and horizontal bar rails should not be used. The planning of the hook mesh is necessary to be safe and reliable, the bolt should be installed on the basis of the railing, its strength should meet the requirements of the standard.

What’s the difference between cold galvanized wire and hot galvanized wire? It is mainly different production process. Cold galvanized iron wire, also known as electric galvanized iron wire, is the use of electrolytic galvanizing process, and hot galvanized iron wire is the use of hot penetration galvanizing process. Compared with the two, hot dip galvanized iron wire thick coating, high zinc content, has stronger anti-corrosion and anti-rust effect. Similarly, the price is also higher, cold galvanized iron wire and hot galvanized iron wire which good? Mainly for the use of scenarios and requirements to choose appropriate galvanized iron wire, appropriate is better.

Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.

4. Keep the rinsing water clean after wire pickling, which is an important link to reduce zinc consumption. The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate.

Decorative hook mesh selection of stainless steel, aluminum alloy, brass, copper and other alloy materials, through the special process of preparation of hook mesh. It is a silk screen made of decoration. Today we introduce the aperture and wire diameter of the decorative hook mesh.

Welding electrode has a wide range of applications, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding.

Many electrogalvanized wire diameter products are formed by wire drawing, wire drawing is a kind of processing technology, can make the product reach the required shape and meet the standard mechanical properties. Cold wire drawing is carried out at recrystallization temperature, hot wire drawing is carried out at crystallization temperature, warm wire drawing is drawn at higher than room temperature and lower than crystallization temperature. Cold drawing is a common drawing method.

If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.

Wire mesh production of general selection of low carbon wire, after fine and accurate active welding equipment processing, the selection of galvanized process surface treatment. After the completion of the product, the net surface is smooth and regular, good integrity, strong and consolidated, even if part of the choice or pressure will not appear lax phenomenon.