Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

Now it is mainly 12 or 14 galvanized barbed rope. Although they are calculated according to the price per ton, the calculation is different when it comes to every meter, because the thickness of the silk is not the same, which causes the problem that one galvanized barbed rope of equal weight is longer and the other is longer. Customers must have detailed communication with the barbed rope factory before purchasing to avoid such problems.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Large roll galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Large roll galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics.

Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.

Hot wire mesh in the building wall engineering mainly played the anti-crack effect, inside and outside the use of specifications are not the same. Hot dipped wire material choose low carbon wire, through automation welding precision machinery processing after forming, surface treatment by zinc immersion process, galvanized barbed wire surface smooth and tidy, uniform structure strong, the overall performance is good, even if the local cutting or under pressure will not loose phenomenon occurs, it is the iron mesh strong anticorrosion performance in one of the widely used net class.

As we all know, even if it is the same kind of steel wire, because of the steel making process, wire drawing process and equipment are not the same, so the quality of steel wire production is not the same. Due to the different mechanical properties of steel wire itself, flattening process and equipment, the width and elongation of steel wire in the flattening process have different effects. Therefore, in the selection of wire diameter, the following three factors should be considered: