The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.

Temporary rust prevention is to prepare for the completion of the mission of the protective layer to be removed. The methods include: cajoling corrosion inhibitors, coating antirust oil, peeling molecular compound plastics, drying air, vacuuming, etc. Change the internal structure of the metal: new chromium, nickel and other alloy elements made of stainless steel, but the alloy is not much, expensive, difficult to produce widespread application.

Advantages: The cost of hot dip galvanized rust prevention is lower than that of other paint coating. In suburban environment, the standard hot-dip galvanized rust prevention thickness can adhere to more than 50 years without repair. In urban or offshore areas, the standard hot-dip galvanized rust protection layer can last 20 years without repair. Galvanized layer and steel is a metallurgical connection, into a part of the steel surface, so the durability of the coating is more reliable.

Now hexagonal net is used in a large number of Bridges, piers and bridge buttress inclined plane protection, bridge buttress inclined plane there are many kinds, people according to the inclination of the inclined plane to choose the right hexagonal net, when the inclined plane gentle, people generally use gabion slope protection system, and in the case of steep slope, people will use gabion mesh gravity protection wall.

The invention technology is used to put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and plays an important measure to stabilize the PH value within a numerical range, and also facilitate the filter filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

The thorn rope belongs to the weaving industry, so it is less affected by environmental protection. The thorn rope will not be discarded in the production process, and it belongs to the weaving industry, so the situation is less affected by environmental protection.

Stainless steel barbed rope in the way of corrosion is not very, because the surface is not treated but rely on its own raw materials for corrosion resistance, so there will be no chemical reaction. After a long time of use, it will not rust like the corrosion layer on the surface of hot dip galvanized barbed rope, because the internal material of stainless steel barbed rope is the same as the material on the surface. The most obvious difference in a short time is the cross section of this piece, hot dip galvanized barbed wire because of surface anticorrosion treatment, so there will be rust in the cross section of this piece, and stainless steel barbed wire because the internal raw materials and surface raw materials are consistent, so there is no such situation.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Even so, when they come out, they make trouble, even though they know they will be punished, but they are only in a cage.) If you have time to refer to some foreign dog books, also strongly advocate cage training as a puppy. Before starting cage training, the cage is padded with a water bottle, some fun toys and bones to chew on. The cage door must be opened. Order the dog into the cage, then lure it into its new den with tasty cookies.

In fact, iron wire has been widely used in our daily life, and it has very good performance. Iron wire production developed earlier because of its simple technology and wide application. Plastic spraying refers to the plastic powder, sprayed on the product of a surface treatment method. Plastic spraying is often referred to as electrostatic powder spraying, the use of electrostatic generator to make plastic powder charged, adsorbed on the surface of the iron plate, and then after 180 ~ 220℃ baking, so that the powder melt and adhere to the metal surface, plastic spraying products are used for indoor use of the box, paint film showing flat or matte effect.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.