Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

6, the use of special formula and special UV absorbent, no fading, no yellowing, no peeling, no cracking, no foaming, no moth, the use cycle can be more than 30 years.

The galvanizing process of galvanized wire products is a very effective metal anticorrosion method. It is also widely used in other industrial fields. The use of galvanized iron wire is very common in metal structure equipment of various industries. Due to the influence of production technology or other factors, the zinc layer of galvanized wire products will be different to a certain extent, especially ordinary galvanized can not reach the beauty of electric galvanized, the zinc layer of ordinary galvanized wire is mainly for corrosion prevention.

Paint on the galvanized layer, the bonding force between each other has a great relationship with the baking temperature of the paint, and alkyd paint is coated after galvanized, and the adhesion is not a problem. After galvanized to do amino paint, paint adhesion is not very good. Do two bottom two surface, adhesion is good, if the two bottom two surface changed to two bottom three surface, that is, more paint, more baked once, again test adhesion is very bad, bad enough to tear the paint from the galvanized layer.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

Galvanized iron wire can be divided into hot-dip galvanized iron wire and cold galvanized iron wire according to different processing methods. Galvanized iron wire is more prominent in its corrosion resistance. Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Galvanized iron wire products are widely used in construction, handicrafts, wire mesh preparation, the production of galvanized hook mesh, wall mesh, highway guardrail, product packaging and daily civilian and other fields.