This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Dip plastic six side barbed wire corrosion lost the original characteristics, in the shape, color and mechanical properties and other aspects will change, resulting in equipment damage, pipeline leakage, in particular, is prone to fracture, lose the original protective function.

In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.