In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

The protective duration of galvanized iron wire is closely related to the thickness of galvanized iron wire. In general, zinc layer thickness needs to be very high in dry main gas and indoor applications, but in harsh environments. Therefore, in the selection of galvanized layer thickness, the impact of the environment should be considered. If galvanized iron wire products of different diameters are required, material selection and coating should be controlled reasonably.

Cold wire drawing is a kind of cold processing of metal. The raw material is wire rod, which is produced by peeling, galvanizing and other processes. Galvanized cold drawing is used more in building materials. Its testing standards are also different. The strength of cold drawing is relatively high. Because of the high strength of steel, it plays a very important role in construction. It saves the construction steel in building materials, and also reduces the cost of the project. It also plays a very important role in the structure of concrete.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

Heavy duty hexagonal mesh made of steel wire by special machinery woven into a hexagonal mesh net. This kind of mesh can be cut and assembled into fence mesh, mountain hanging mesh, vegetation three-dimensional mesh, composite, etc. Aliases: Gabion mesh, heavy hexagonal mesh, ecological mesh, wire mesh, etc.

Plastic-coated barbed rope is not only used but also beautiful, so it is used in a large number of highway sides, and other special places, so what are the colors of plastic-coated barbed rope? Where are the plastic-coated thorn ropes of no color respectively applied?

If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.

The wire used for wire mesh is made of low carbon steel wire, medium carbon steel wire, high carbon steel wire, stainless steel wire and other materials woven or welded. Production technology: general braid, embossed braid and spot welding type. If the steel wire as the material, after the equipment processing into a network, so called wire mesh.

The bonding and anchoring function between the cold rolled ribbed steel bar and concrete is outstanding. In reinforced concrete structure, the width of black iron wire processing crack is smaller than that of circular steel bar, even than that of hot rolled thread steel bar. Therefore, it is used in the component, which fundamentally eliminates the phenomenon of steel wire sliding and damage, and improves the load bearing ability and crack resistance ability of the component end.

Thorn rope factory production per ton of product profit is not particularly high so in the sales price to wholesale, many users always think that thorn rope price has a lot of profit space so they are eager to lower the price, some manufacturers in order to sell out on the use of low price promise and then underweight behavior. Often the actual user spends less money with the lack of weight is almost the same, so the unit price is relatively high. Because the quotations of the thorn rope factory are in accordance with the real price, the quality is guaranteed. In this way, the customers will not look for debts after the purchase, and the subsequent purchase work will still find us, so that we can benefit.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

The large roll of galvanized silk should be coated with oil, the fiber core is dipped in oil, and the grease should be able to protect the fiber core from decay and corrosion, the iron wire moistens the fiber, and lubricates the wire rope from the inside. The surface is coated with oil so that all the wire surface in the rope strand is evenly coated with a layer of anti-rust lubricating grease, which is used for the mine rope with friction lifting and mineral water, to be coated with black grease with increased wear and strong water resistance. Other uses are coated with red oil oil with strong film and good rust resistance, and require it to have a thin oil layer, which is easy to keep clean during the operation.

Although galvanized iron wire has the protection of galvanized layer, it does not say that it will not rust at all, but delays the time of rust. In general, cold galvanized iron wire can be kept for 1-2 years without rust, hot galvanized iron wire can be used for 8-10 years without rust. If properly maintained, the use time will be longer. So how to prevent galvanized iron wire rust?