Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

Before wall plastering, the wall column is connected to the gap construction wire mesh, which can play a certain strengthening and heat preservation effect. The mesh is hung on the interface surface of different grassroots, and the length of each side should meet the requirements of 100mm, so as to prevent shrinkage and cracking caused by different grassroots. Mesh wire diameter can also determine the effect and efficiency of construction, mesh fine laid up convenient soft, high construction efficiency; Of national standard can assure quality, but laid respect is inferior to fine construction fast.

With the development of mining industry, pig iron classification in Our country has been very extensive, to meet the needs of the machinery industry. Generally speaking, iron wire factory produces galvanized iron wire iron can be divided into two categories, is directly from the iron ore through iron tracing exercise out of the metal, the primary components of the ore is iron oxide, silica and other miscellaneous stones. When this ore is specially refined into metal iron, the elements such as carbon, silicon, manganese and so on are mixed in, so that the refined data is called – like general pig iron, also for the initial grade of the material.

Bridge protection system generally do not need to be specially installed special drainage system, the use of hexagonal mesh made of gabion mesh box, the inside of the filler are selected stones, these stones are not easy to wear, and between the stones and stones will retain some gaps, so it is very good to meet the drainage requirements.

Because of the corrosion resistance of zinc layer, can be applied to all kinds of environment, it is also very convenient to use, has been a more popular hardware products. Galvanized iron wire should pay special attention to the acyl wash, to slowly into the container, to prevent acid sputtering on the body, at the same time prohibit the water into, so it is easy to let the acid out, to learn to handle lightly, stacking should also be firm and neat. It can be widely used in construction, handicrafts and other daily civilian applications.

When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.

Different from double strands of barbed wire to install directly on the ground, the blade thorn rope is fixed on some affiliate products just again, as was the case according to the common on the wall, often wall width is far lower than the diameter of the blade thorn rope under the premise of no such device is fixed in place, use special stents to prevent blade thorn rope can better protect us.

Breeding cattle and sheep with barbed rope effect is better, because the advantages of barbed rope are more. So the thorn rope used to do animal husbandry effect is good?

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.