On the highway, barbed rope protection net is generally to prevent people and animals from crossing the highway at will, so as not to interfere with driving and reduce accidents, as well as effectively prevent illegal occupation of road land and other issues of traffic safety facilities. There are many forms of barbed rope protective nets, commonly used metal, woven net, barbed wire and often green gracilaria. Metal braided net is set in crowded areas, barbed wire is used in areas with few people and animals, and the structure of hedges and barbed wire is used in toll stations and service areas. In the past two years, considering the beauty of the problem, in the Pearl River Delta region of some highways with fruit plastic spot welding network (usually said guardrail network), this barbed rope protection network is more good-looking, durable, the overall effect is good, but the construction requirements are higher, more expensive. General sections should not be used, in the city center, scenic spots or strong requirements for beautiful sections can be used.

(2) Packing and binding galvanized shaft wire order notes: ① the galvanized iron wire shall not be damaged when the tightening. (2) Stop the use of more than two strands of galvanized iron wire around the operation method. ③ The diameter of galvanized wire for pulling should not be less than 4mm, and the diameter of galvanized wire for binding should not be less than 2.6mm. (4) Galvanized iron wire shall not be used as waist hoop down reinforcement, usually not used as a whole binding. Warehouse galvanized wire is mainly used to block and distinguish the function of the area, warehouse galvanized wire is one of the primary use of galvanized wire, warehouse galvanized wire primary layout features are as follows: layout: Column mesh frame, column to choose square steel pipe, galvanized wire frame is also a small square pipe as the data, column and mesh frame corresponding direction are welded connecting ear piece (flat iron), column and mesh frame through the connection of the ear piece bolt fixed, column bottom welding plate, column bottom plate through expansion bolts and fixed on the ground.

6, according to the wire diameter thickness to adjust zinc dipping time. Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is the length of the distance between the lead screw on the zinc pot and the ceramic sinking roll. The zinc dipping time of coarse wire diameter should be long, and the zinc dipping time of fine wire diameter should be short.

Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.

The protective duration of the galvanized layer of large roll galvanized wire is closely related to the thickness of the coating. Generally speaking, in relatively dry main gas and indoor use, and in harsh environmental conditions, the thickness of galvanized layer needs to be very high. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance.

The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. The extracted zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the biggest steps to bring zinc consumption down, and it’s a real problem, one that hasn’t been solved for years.