The advantages of hexagonal net to do jet hanging net, the first is that the processing speed is fast, the cost is low, and it is very good to roll out when it is open because of the edge. Common specifications: 12 cm x15 cm (11cm x11 cm) 11 cm x15 cm (10 cm x10 cm) 10 cm x12 cm (9 cm x9 cm) 9 cm x13 cm (9 cm x9 cm) 8 cm x10 cm (7 cm x7 cm) common wire: 1.3mm 1.4mm 1.5mm 1.6mm 1.7mm 1.8mm 2.0mm 2.3mm 2.5mm Commonly used materials: galvanized wire hot dip galvanized wire to wire drawn zinc aluminum alloy plastic coated wire stainless steel wire.

After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

Hot drawing is the heating before the wire enters the die hole, mainly used for high melting point wire drawing; The temperature drawing is carried out by heating the heater to the range of temperature, mainly used for galvanized steel wire, difficult to deform drawing.

The large roll of galvanized silk should be coated with oil, the fiber core is dipped in oil, and the grease should be able to protect the fiber core from decay and corrosion, the iron wire moistens the fiber, and lubricates the wire rope from the inside. The surface is coated with oil so that all the wire surface in the rope strand is evenly coated with a layer of anti-rust lubricating grease, which is used for the mine rope with friction lifting and mineral water, to be coated with black grease with increased wear and strong water resistance. Other uses are coated with red oil oil with strong film and good rust resistance, and require it to have a thin oil layer, which is easy to keep clean during the operation.

If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.

Unless the stainless steel blade barbed rope is specially customized, it is usually produced by the mould with the knife length of 22mm, which is the BTO-22 type we usually call. This is not necessarily the specification from 11mm to 65mm are specifications. Unless the customer insists on customized length requirements, the barbed rope manufacturer will produce BTO-22 stainless steel blade barbed rope.

Titanium alloy with low carbon content is obtained because the carbon content remains the original concentration. The hardness of titanium alloy is mainly related to its carbon content. Therefore, after carburizing and subsequent heat treatment, the workpiece can obtain the performance of hard and tough inside. Galvanized wire varieties are mainly classified into three categories: electric galvanized wire, hot galvanized wire and galvanized wire. Among them, the classification of galvanized wire is divided into large roll galvanized wire, medium roll galvanized wire, small roll galvanized wire, galvanized shaft wire, truncated galvanized wire and other main production varieties.

Although galvanized iron wire has the protection of galvanized layer, it does not say that it will not rust at all, but delays the time of rust. In general, cold galvanized iron wire can be kept for 1-2 years without rust, hot galvanized iron wire can be used for 8-10 years without rust. If properly maintained, the use time will be longer. So how to prevent galvanized iron wire rust?

When large rolls of galvanized wire are used to bind and reinforce the goods, corresponding binding methods should be selected according to the fastening node conditions of the strengthened goods, such as opening binding, opening binding, insertion binding and so on. The insulation layer of semi-hard and soft insulation products shall be based on the diameter of the steel pipe and the size of the equipment. Large rolls of galvanized wire or glue are tied together with a width of 60mm. The binding interval of semi-hard insulating products shall not exceed 300 mm; The larger length of felt and cushion shall not exceed 200mm, and the number of belts shall not be less than 2.