Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging.

When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.

The diameter of cold-drawn wire should conform to the contract, check whether the amount of zinc meets the requirements of the contract, check the tensile strength, and ask the factory to provide the corresponding inspection report. The wire factory introduces that the weight of a single coil of wire of different specifications should not be lower than the volume weight required by the contract, and record the value. No contacts are generated for each reel of wire. If there are contacts, no more than three contacts are generated for each reel. Each contact should be smooth surface treatment, the wire can not be pulled off from the contact, in line with customer packaging requirements.

A. When the thickness of the plating is 3-4 mm, the zinc adhesion should be less than 460g/m, that is, the average thickness of the zinc layer is not less than 65 microns.

If the zinc coating is good, but in 3% nitric acid when the light, the coating has dark shadow, passivation occurs when the film is brown, may be caused by foreign metal impurities such as copper or lead in the galvanizing liquid. When problems occur in the process of galvanizing large coil galvanized wire, the temperature and current density are checked first, and then the content of zinc and sodium hydroxide in the plating solution is measured and adjusted through the analysis of the plating solution. Whether DPE content is low can be determined by hull cell test.

Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

Galvanized wire mesh is divided into hot dip galvanized wire mesh and cold galvanized wire mesh. Galvanized steel wire net selects the high quality low carbon steel wire, iron wire factory made by precision of automation machinery welding technology processing, smooth surface, firm structure, integrity is strong, even if the local cutting of galvanized steel wire net, or local also under pressure from loose phenomenon, after molding, wire mesh galvanized corrosion resistance good, has the advantage that the general steel mesh does not have.

Custom is made of low carbon steel silk woven, mesh structure he has the characteristics of corrosion resistance, high strength and ductility. Steel wire diameter up to 2.0mm-4.0mm, steel wire appearance is usually selected hot dip galvanized maintenance, galvanized maintenance layer thickness can be made according to customer needs, galvanized maximum can reach 300g/㎡.

Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device. In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc.

This process has no mold, low processing cost, easy forming, can process a variety of shapes and other characteristics are widely used. But the products of the guardrail are powder impregnated plastic. According to whether it needs heating, it is divided into hot dipping and cold dipping. According to the raw materials of dipping, it can be divided into liquid dipping and powder dipping. Hot-dip galvanizing, as a metal anticorrosion method, is usually to put the steel structure to be derusted into the zinc liquid at about 500℃, so that the zinc layer is attached to the surface of the steel structure.