The quality of hot-dip galvanized barbed wire is only good in the surface of the wire attached to the galvanized layer, and with the chemical reaction, the surface of the zinc layer will gradually lose effect because of the oxidation reaction, this situation is more prominent in the humid area of the environment. And because after all, it is rusty iron wire, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

(1) The application method of packaging and binding galvanized shaft wire ordering: ① the pulling position on the goods should be reasonably selected. When used to avoid horizontal movement of goods, the pulling position should be as low as possible; When used to avoid overturning the goods, the pulling position can be appropriately high. ② The use of galvanized iron wire [1] pull reinforcement methods mainly include: figure eight, inverted figure eight, cross, zigzag or reverse zigzag and so on. Various pull methods can be used alone, but also two or more than two kinds of use. The pull should be as symmetrical as possible. (3) When pulling reinforcement, the single or double strands of galvanized iron wire will reciprocate around the goods and vehicles between the two tying nodes, and should be pulled tight galvanized iron wire so that the tightness of each strand is as common as possible, and some of the remaining cross around its own rope rod, and the rest of the tail toward the car.

1, galvanized wire mesh molding sheet must be packed with flat hard data, to avoid eternal deformation due to poor packaging.

(1) The application method of packaging and binding galvanized shaft wire ordering: ① the pulling position on the goods should be reasonably selected. When used to avoid horizontal movement of goods, the pulling position should be as low as possible; When used to avoid overturning the goods, the pulling position can be appropriately high. ② The use of galvanized iron wire [1] pull reinforcement methods mainly include: figure eight, inverted figure eight, cross, zigzag or reverse zigzag and so on. Various pull methods can be used alone, but also two or more than two kinds of use. The pull should be as symmetrical as possible. (3) When pulling reinforcement, the single or double strands of galvanized iron wire will reciprocate around the goods and vehicles between the two tying nodes, and should be pulled tight galvanized iron wire so that the tightness of each strand is as common as possible, and some of the remaining cross around its own rope rod, and the rest of the tail toward the car.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

Some customers pay more attention to the quality problem, so they pay more attention to the service life. The barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

Stainless steel material refers to air, steam, water and other weak corrosive medium and acid, alkali, salt and other chemical corrosive medium corrosion of steel, also known as stainless acid-resistant steel. In practical application, the steel that is resistant to weak corrosive medium is often called stainless steel, and the steel that is resistant to chemical medium corrosion is called acid resistant steel. And galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 grams/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance. Products are widely used in construction, handicrafts, silk mesh, highway fence, product packaging and daily civilian and other fields.

The invention technology is used to put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and plays an important measure to stabilize the PH value within a numerical range, and also facilitate the filter filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.