The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.

After annealing, the extension rate of galvanized wire is increased, making the product more soft and increasing the scope of application of galvanized wire. After electric galvanized hot galvanized, electroplated copper and other widely used screen production. Building reinforcement binding with galvanized wire mesh braided with the first after plating, plating and other methods, after treatment of galvanized wire mesh or steel wire mesh, has good corrosion resistance, oxidation resistance characteristics, can be used in construction, petroleum, chemical, aquaculture, garden protection, food processing and other industries reinforcement, protection and heat preservation.

The wire diameter of raw materials used in different types of barbed rope is also very different, but in the production and processing process of barbed rope need to know the amount of use.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.

The common weight standard of galvanized barbed rope is 25kg per coil, and the length of each coil varies from 220-250 meters according to the specifications of the barbed rope. And of course we all know that the heavier the disc the longer it is. But there is one point that is worth our attention, that is, the hollow inside the general larger disk is relatively small, and the hollow inside the lighter galvanized thorn rope is relatively large. The purpose of this is to reduce the number of bending of the thorn rope and make it easier and more beautiful when installing, on the other hand, it looks larger in appearance.

Hexagonal mesh is made of galvanized iron wire woven by automatic mesh machine, mesh into regular hexagonal, mesh standard, beautiful, mesh size can be customized according to customer requirements, usually 27mm,20mm, 13mm, wire diameter from 0.40mm to 1.20mm, to meet the requirements of different customers.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.