Domestic iron wire factory has been able to consume wire rope, radial low steel wire, umbrella steel wire, spring steel wire, bicycle saddle spring steel wire and other products. In the 1980s, hot – plated low carbon steel wire, fan net cover steel wire, carbon structure steel wire, bed steel wire and so on were also published. The elongation of wire is increased after annealing. Make the product more soft and increase the scope of application of the wire.

Now most people want to choose a few when choosing barbed wire material better thorn rope, but the special barbed wire the better, not right, it is important to choose which model is most suited to their own thorn rope,, although is very simple product, but in the use of these products are for specific situation is different, and has a different effect, Maybe now consumers do not have too much concept of blade barbed rope, in fact, such barbed rope products have a higher safety factor.

Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

Annealing wire is widely used mainly because it has a good elasticity and flexibility, in the annealing process can be a good control of its hardness and softness, it is mainly made of iron wire, more commonly used in the construction industry tie wire use. When the wire factory is in production, the annealing wire will be processed according to the performance of the material, and its hardness will be changed according to the different demand, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production.

3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag

Ordinary blades installed on the walls of the barbed wire fence height in two metres of general construction cost in more than a dozen yuan a metre, but if the prison on the height of the wall construction modest have already reached the four or five meters so that every one meter of the cost of construction in 30-40 yuan, mainly because the work high above the risk is bigger. The construction cost is different, but the price of the blade barbed rope is the same. The construction cost is often higher than the product. In this way, the blade barbed rope factory recommends customers to use the blade barbed rope with better quality to avoid the tedious time and cost of subsequent removal and installation.

Galvanizing is a process of coating a metal surface with zinc in an electrochemical reaction on the metal surface to improve the corrosion resistance of the metal. Wire drawing is a process in which metal materials are drawn by mechanical methods to reduce their cross-sectional area and increase their length. So, the combination of galvanized to wire drawing two processes, what impact on the performance of the product?

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.

Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.