There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.

Now it is mainly 12 or 14 galvanized barbed rope. Although they are calculated according to the price per ton, the calculation is different when it comes to every meter, because the thickness of the silk is not the same, which causes the problem that one galvanized barbed rope of equal weight is longer and the other is longer. Customers must have detailed communication with the barbed rope factory before purchasing to avoid such problems.

Because zinc layer corrosion resistance, can be applied to all kinds of environment, use is also very convenient, has been more popular hardware products. Galvanized iron wire should pay special attention to the acyl washing, to slowly put into the container, to prevent acid sputtering on the body, and prohibit the water into the water, so that it is easy to let the acid out, to learn to handle gently, stacking should also be firm and neat. It can be widely used in architecture, handicrafts and other daily civilian applications.

In use, there is no need for daily maintenance and maintenance, not only can save a lot of time, but also can reduce costs, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different types, can choose according to their own needs. With good flexibility and elasticity, the main role of annealing wire is to control its degree of softness and hardness, in the production of annealing wire is made of steel wire, now more used in the construction industry binding use, compared with ordinary wire is also more soft, have better luster.

The distance between the adjacent two thorn rope installation do not know whether you have noticed? Careful observation can find that its spacing is not the same, the thorn rope factory for customer consultation when asking the installation height of the reason.

The spray blade has strong adhesion and mechanical strength, and is widely used in the isolation and protection of the boundary of grassland and railway, as well as the protection of garden apartments, units and prisons. The following Haorong for you to introduce the characteristics of spray blade rope.

Compared with other galvanizing processes, galvanized steel wire has low cleaning requirements before plating. However, under the current trend of increasing the quality level of galvanized layer, some pollutants brought into the plating tank are obviously harmful. Because cleaning galvanized coating wastes a lot of time and reduces production, it is very important to properly clean and effectively rinse the substrate before electroplating.

Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need to have the condition of many sided, just need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer does not meet the strength requirements in the data, after all, there is no way to make the strength of the product progress, so this is the necessary condition.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.