Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

Its wire diameter specifications include: 8#-24#, with thick coating, corrosion resistance, strong coating and so on. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire. Low carbon steel wire is called galvanized iron wire after drawing and galvanized, so galvanized wire products have certain characteristics. In order to better let galvanized wire play an effect, in the process of galvanized wire, generally according to customer needs to control the thickness of galvanized wire zinc layer, so that galvanized wire can meet the needs of customers.

If not packaged, then a car of blade thorn rope can not be loaded with many pieces, but also relatively occupied places and easy to be lost in the process of transportation. Each bundle of blade barbed rope is 50 bundles. After hydraulic compression, the volume is reduced and it is more convenient to load and unload. Forklift trucks can load and unload easily. In general, when exporting, the blade thorn rope will be packaged for sale, so that the volume occupied in the container is relatively small, which can be very easy to size and place will not take up much place.

The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

Spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and resistance to impact and oscillation. The strength and endurance objectives, especially to prevent the occurrence of modification cracks, are the key to the consumption of spring wire. The inner quality and outer quality of the wire rod directly affect the function of the wire.