Most cattle nets are mechanically woven from high ductibility and corrosion resistant low carbon steel wire or PVC coated steel wire. The manufacture of cattle net several common raw materials are generally galvanized wire, hot dip galvanized wire, galfan steel wire plating, ten percent aluminum zinc alloy steel wire and the new selenium chromium wire plating.

Therefore, the rust of galvanized black iron wire has a great relationship with storage. At the same time, after rust, it should also be reasonable for post-treatment to avoid affecting its use effect. Of course, when the black iron wire is galvanized, the thickness of the galvanized layer should be ensured, so that the possibility of rust can be reduced. Speaking of galvanized iron wire, perhaps many people think it is relatively rare, in fact, it is not.

A pet carrier can be used as an indoor or outdoor pet house. The dog cage is equipped with a fixed food basin and water fountain, and the foot plate pet cage rubber pad has bayonets on four sides to be splintered. It can be spliced, cut and disassembled according to the size of the cage. It is convenient and easy to clean. It can solve the problem of pinching the feet of the puppies in the ordinary cage and prevent the puppies from causing adverse reactions in the development. The dividers are breathable and comfortable, and can be used as heat shields for pets in summer. A puppy with small feet, no feet, no pinching.

Annealing wire is widely used because it has a good elasticity and flexibility, in the annealing process can be good control of its hardness, it is mainly made of iron wire, more often used in the construction industry binding wire use. In the production of the wire factory, annealing wire will be processed according to the properties of the material, according to the needs of different to change its hardness degree, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time. However, because the plating solution contains highly toxic cyanide, the gas escaping in the plating process is harmful to the health of workers, and the waste water must be treated strictly before discharge.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Temporary rust prevention is to prepare for the completion of the mission of the protective layer to be removed. The methods include: cajoling corrosion inhibitors, coating antirust oil, peeling molecular compound plastics, drying air, vacuuming, etc. Change the internal structure of the metal: new chromium, nickel and other alloy elements made of stainless steel, but the alloy is not much, expensive, difficult to produce widespread application.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.