Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

The size of the galvanized layer of galvanized iron wire is related to the anti-corrosion ability and application effect of galvanized wire. The thickness of the galvanized layer of the general standard galvanized wire products should be tested after the product is formed. There are three specific test methods. Weighing method and cross section microscopy method are destructive experimental methods, and magnetic method is a relatively rigorous non-destructive method, but the measurement steps and requirements are relatively high, so they are rarely used in specific applications. The first two methods are intuitive and common methods.

The price of galvanized iron wire performance is the key to win, galvanized wire only with good performance, in order to win the market, in order to obtain customer praise. In galvanized wire, the main function of carbon in increasing hardness, less is less easy to rust, the main function of chromium is acid and alkali resistance; Nickel’s main function is high temperature resistance, acid and alkali resistance and conductive use; The main function of iron is magnetic conductivity; The main functions of titanium are low density, high hardness and strong corrosion resistance. The main function of copper is magnetic and electrical conductivity. Different chemical components have different functions, which together form the characteristics of galvanized wire.

The lighting surface of each type of shed is designed to be curved, improving the Angle of the light surface, because the lighting surface is curved, no dust accumulation, good light transmittance, high temperature in the shed, after measurement, the average temperature in the shed is 3℃ higher than the traditional bamboo pole cement column shed, the yield is increased by 15~20%, and the harvest date is advanced. The formula is scientific, the surface does not absorb moisture, do not return halogen through modification technology and scientific production process, solve the greenhouse frame rod is easy to absorb moisture return halogen, poor water resistance and easy to change the shortcomings, so that the greenhouse steel pipe in the high temperature and high humidity environment, few drops, frost phenomenon, and reduce pests and diseases.

According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

In daily life, what we can bend by hand is basically galvanized iron wire, not steel wire. It has a high zinc content, which ensures its good toughness and resilience, but also has ultra-high corrosion resistance, which can last for decades in outdoor environments. There are many practicability of galvanized iron wire, such as strong reliability, galvanized layer and iron together, form a special metallurgical structure, in the use and transportation process, can ensure that will not be mechanical damage.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.