Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

Iron and steel in the condition of cooling on the surface galvanized, and hot dip galvanized steel pipe in the condition of hot dip on the surface, its adhesion is strong, not easy to fall off, hot dip galvanized pipe although also rust phenomenon, but in a long period can meet the technical and sanitary requirements.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

Many pet cages are designed with a small box in the base, so that pets can clean up when they poop, but also convenient for pets’ health. For example, if there is no excreta box, pet excreta will be on the ground, which is quite unhealthy. If you have a box, it’s easy to take the box out and wash the trash away so it doesn’t get all over the place, so it’s more hygienic.

Strictly control the pH value of large roll galvanized wire bath, research shows that the size of the bath pH value directly affects the quality of steel wire coating, improper control of pH value will cause loose coating. When the pH value is greater than 3, the steel wire coating has burr caused by fine dendrites, and the surface is not smooth. The current density is strictly controlled. From the microscopic morphology, the higher the current density, the larger the zinc layer grain deposition, the less dense the corresponding zinc layer.

Electric welding net is also known as external wall insulation wire mesh, galvanized wire, galvanized electric welding net, wire mesh, row welding net, touch welding net, construction net, external wall insulation net, decorative net, wire mesh, square eye mesh, screen mesh, anti-crack mesh. Stainless steel electric welding mesh, is made of high quality stainless steel wire row welding, more acid resistance, alkali resistance, welding firm, beautiful, widely used and so on.

With the improvement of people’s living standards, kittens, dogs and other small pets also need a stable nest, pet cage has become a more important choice for people to raise pets. Suitable cat cage, dog cage is very necessary for kittens and dogs. There are many kinds of pet cage, cat cage, dog cage selectivity is relatively large, pet cage is generally made of thicker wire, and then get a base with wheels at the bottom, such a simple pet cage is made.

Annealing wire is widely used mainly because it has a good elasticity and flexibility, in the annealing process can be a good control of its hardness and softness, it is mainly made of iron wire, more commonly used in the construction industry tie wire use. When the wire factory is in production, the annealing wire will be processed according to the performance of the material, and its hardness will be changed according to the different demand, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.