When the coating of large galvanized wire is blistered in the process of galvanizing, the bath temperature should be checked first. If the bath temperature is not low, and then strengthen the removal of oil before plating, to prevent the base metal in acid corrosion. If you pay attention to these problems, the bubbling phenomenon still exists, it should pay attention to the dosage and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, to reduce the content of additives, observe whether the bubbling phenomenon is improved. If there is no improvement, check whether the additive has been stored for too long or whether it contains too many impurities.

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.

The main raw material of blade barbed rope is galvanized wire and galvanized sheet, because the price of galvanized sheet is more expensive than galvanized wire, so it is directly reflected in the price of the sales of blade barbed rope. There is also the difference in processing technology also led to the difference in the price of the blade thorn rope. The traditional barbed rope is mechanically twisted, which uses less labor and has high production efficiency. But the blade is after two mechanical processing in the manual processing operation before the appearance. So whether from the labor force or from the production efficiency also said there is a large gap. These factors lead to the price of blade thorn rope is more expensive the main factor.

In reinforced concrete structure, the crack width of cold wire drawing is smaller than that of circular steel bar or even that of hot rolled thread bar. So cold wire drawing is more popular in the construction industry. The material for cold drawing is made of steel bars and can be simply explained how it is made, that is, its production process is simple. It’s based on steel bars, which are constantly stretched evenly, stretching the bars into something very thin, like wire drawing, without plasticity.

Spray powder mainly acrylic powder, polyester powder and so on. Dipping is a kind of plastic coating process, that is, the plastic coating on the matrix, generally metal, such as: daily use of clothes hangers, pliers handles, scissors on the rubber sleeve, various handrails, etc. Plastic immersion is to heat the metal to spray plastic powder evenly on the metal to form a plastic film, or heat immersion liquid into the metal to cool it and then plastic coating on the metal surface.

6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need yo have a variety of conditions, will need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer in the data does not fit the strength requirements, after all, there is no way to make the strength of the product progress, so this is the condition to.

Thorn rope factory can not only have one type of product when processing thorn rope, a variety of models can meet the protection needs of different customers.

Now the production of stainless steel blade barbed rope unless it is a specially customized model, under normal circumstances are the use of a knife length of 22mm mold production, that is, we usually say bto-22 type. It’s not necessarily the case that there are specifications from 11mm to 65mm. Unless the customer insists on customizing the required length, the barbed rope manufacturer produces bto-22 stainless steel blade barbed rope.