In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

Due to the implementation of the grassland contract operation obligation system, herdsmen have a high capacity to strengthen and raise their stainless steel barbed rope fence net in grassland pastoral areas, forming the phenomenon of high density and high height of stainless steel barbed rope fence net in grassland pastoral areas, which is destructive and even destructive to the survival of wild animals.

Stainless steel blade barbed rope material is produced according to stainless steel plate and stainless steel wire, as a whole have achieved the purpose of high quality anticorrosion. So how long can stainless steel blade thorn rope be used?

The quality of hot-dip galvanized barbed wire is only good in the surface of the wire attached to the galvanized layer, and with the chemical reaction, the surface of the zinc layer will gradually lose effect because of the oxidation reaction, this situation is more prominent in the humid area of the environment. And because after all, it is rusty iron wire, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

Unless the stainless steel blade barbed rope is specially customized, it is usually produced by the mould with the knife length of 22mm, which is the BTO-22 type we usually call. This is not necessarily the specification from 11mm to 65mm are specifications. Unless the customer insists on customized length requirements, the barbed rope manufacturer will produce BTO-22 stainless steel blade barbed rope.

Cold galvanizing is also called electric galvanizing. It is the use of electrolytic equipment to remove oil, pickling, and then put the pipe into the solution of zinc salt, and connect the anode of the electrolytic equipment, place zinc plate on the opposite side of the pipe, and connect the positive pole of the electrolytic equipment to the power supply. A layer of zinc is deposited on the pipe fitting by directional movement of an electric current from the positive pole to the negative pole. Cold plated pipe fitting is processed before galvanizing.