In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

Hot dip galvanized wire is used in carbon structural steel, which is processed by drawing and hot dip galvanized. It is widely used in the manufacture of wire mesh, highway guardrail and construction projects. Electro galvanized wire is a kind of metal conforming material made of low carbon steel as core wire by wire drawing and electro galvanized process. Mainly used in wire mesh, highway guardrail and construction projects.

Electric galvanized wire is dipped in the zinc solution of heating ablation, the production speed is fast, the coating is thick but not uniform, the market allows a low thickness of 45 microns, up to 300 microns or more. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.

Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device. In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc.

Cold wire drawing is a kind of cold processing of metal. The raw material is wire rod, which is produced by peeling, galvanizing and other processes. Galvanized cold drawing is used more in building materials. Its testing standards are also different. The strength of cold drawing is relatively high. Because of the high strength of steel, it plays a very important role in construction. It saves the construction steel in building materials, and also reduces the cost of the project. It also plays a very important role in the structure of concrete.