The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.

To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the amount of surface-active substances brought in to Z. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Pet cage has many types, and selective is bigger, pet cages are generally made of wire, with better coarse, then at the bottom with a wheel base, such a simple pet basket was made, in the wheel at the bottom of the mount is for the convenience of the mobile, a pet cages should also adapt to the location of the production in addition to a door, It is convenient for feeding pets.

Hexagonal mesh is a metal wire woven Angle mesh (hexagonal) made of wire mesh, the use of metal wire diameter is based on the size of the hexagonal and different. Also known as: twist flower net, stone cage net, gabion net, flood control network.

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

The protective duration of galvanized iron wire is closely related to the thickness of galvanized iron wire. In general, zinc layer thickness needs to be very high in dry main gas and indoor applications, but in harsh environments. Therefore, in the selection of galvanized layer thickness, the impact of the environment should be considered. If galvanized iron wire products of different diameters are required, material selection and coating should be controlled reasonably.

The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.