Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.

The characteristics of these cages are small, light, easy to carry and easy to clean. For small animal cage, the wire diameter of the general iron wire is not very large, the thickness of the plastic is relatively thin, so the use of the time can not be “violence”, otherwise the cage in the “destruction” will occur under the welding or plastic crack.

The protective duration of galvanized iron wire is closely related to the thickness of galvanized iron wire. In general, zinc layer thickness needs to be very high in dry main gas and indoor applications, but in harsh environments. Therefore, in the selection of galvanized layer thickness, the impact of the environment should be considered. If galvanized iron wire products of different diameters are required, material selection and coating should be controlled reasonably.

Generally, the main reasons for the rust of iron wire are: when the steel mesh in the metal mesh appears some dust, this time you can use some water or alkaline solution cleaning. Followed by floating iron or embedded iron, iron will rust, connected to the stainless steel plate mesh of iron rust, so these iron must be dealt with, can use carbon steel wire brush can also be used for processing carbon steel and so on. Then is the scratch, for the scratch, mainly in the production process, need some stubborn iron scratch stainless steel plate net special polishing cleaning machine.

Electric galvanized shaft wire direct selling is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.

There are many categories of large rolls of galvanized wire, and different categories can be applied to different scenarios. The common application of galvanized iron wire is the application of the construction industry. One is the use of binding wire. Whether it is the binding of scaffolding or reinforcement, galvanized iron wire is needed to carry out. There are also 20kg or 50kg bundles of No. 18, No. 16, No. 14, No. 12, No. 10 galvanized coils.