5, according to the wire diameter thickness to adjust zinc dipping time

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Advantages: The cost of hot dip galvanized rust prevention is lower than that of other paint coating. In suburban environment, the standard hot-dip galvanized rust prevention thickness can adhere to more than 50 years without repair. In urban or offshore areas, the standard hot-dip galvanized rust protection layer can last 20 years without repair. Galvanized layer and steel is a metallurgical connection, into a part of the steel surface, so the durability of the coating is more reliable.

Every galvanized wire production into the peak season of the industry, the road to the factory will from time to time see transportation wire and container container vehicles, as well as galvanized bright silk short-distance transportation trucks, led to the utilization of labor in the surrounding countryside, solved the employment problem of most people. Galvanized wire is divided into hot plating wire and cold plating wire.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

There are many ways to choose the blade stabbing rope, and it is necessary to choose reasonably when choosing. Blade barbed rope is very good in the market reputation, and different types of blade barbed rope can play different roles, so how should we choose blade barbed rope? What are the main points?

After the optimization of the process, mass production of 0.80mm electro galvanized steel wire electro galvanized zinc layer quality is controlled within 80 ~ 90g/m2, zinc layer quality dispersion is very small; The results show that the average weight of zinc layer is 14.5g/m2, the loss of zinc layer is less than 5%, and the tensile strength of steel wire is 2300 ~ 2500MPa. It not only effectively controls the quality of zinc layer of raw steel wire, but also reduces unnecessary waste and production cost.

There are many categories of large rolls of galvanized wire, and different categories can be applied to different scenarios. The common application of galvanized iron wire is the application of the construction industry. One is the use of binding wire. Whether it is the binding of scaffolding or reinforcement, galvanized iron wire is needed to carry out. There are also 20kg or 50kg bundles of No. 18, No. 16, No. 14, No. 12, No. 10 galvanized coils.

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.

1. Zinc pot operators must stick to their posts