Galvanized iron wire has good anti-corrosion and anti-rust ability, so it can be prevented from being used in some outdoor guardrail or fence, especially on handicrafts, handicrafts are also of great use, galvanized iron wire, the surface is not easy to rust and oxidation. Now many hardware manufacturers produce iron wire, and iron wire is very easy to rust, if you need to use in outdoor or humid places, generally customers will require the use of galvanized iron wire equipment to give the wire a layer of zinc, the thickness can be determined according to user requirements.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

Hot-dip galvanized wire is widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries. It has been widely used in recent years in agricultural fields such as agricultural medicine sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and so on.

Large roll galvanized wire welding net is made of high quality galvanized wire welding net, wire through the current, after mutual melting, strong connection point, and the formation of metal mesh. In the use of galvanized iron wire to find the thickness and soft and hard to the size of flowers, weight and softness corresponding to the degree, too soft florets to use fine wire, and heavy flowers, flowers with thick stems to use thick wire.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

Now it is more used in the binding of the construction industry. Compared with ordinary iron wire, it is softer and has better luster. Use in daily life does not need to carry out maintenance and maintenance, save a lot of time, but also save the cost of maintenance and maintenance. Annealed wire has good stability, good corrosion resistance, greatly prolonging the service life. More kinds, can be selected according to different uses, making annealing wire device is simple, improve the utilization rate of the device. The material properties of annealed wire can meet different processing requirements.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

A part of the customers always think that if the price is low to buy the barbed rope products, but often this time to buy the product quality or weight is not up to standard.

As we all know, even if it is the same kind of steel wire, because of the steel making process, wire drawing process and equipment are not the same, so the quality of steel wire production is not the same. Due to the different mechanical properties of steel wire itself, flattening process and equipment, the width and elongation of steel wire in the flattening process have different effects. Therefore, in the selection of wire diameter, the following three factors should be considered: