Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

After electric galvanizing hot galvanizing. Electroplated copper and other common applications of screen consumption. The weaving of the binding of the building steel wire mesh has the first braided after plating, plating after weaving and other methods, after the disposal of the wire mesh or wire mesh has good corrosion, oxidation resistance characteristics, can be used in the construction, petroleum, chemical, aquaculture, garden protection, food processing and other industries of reinforcement, protection and insulation.

Decorative hook mesh selection of stainless steel, aluminum alloy, brass, copper and other alloy materials, through the special process of preparation of hook mesh. It is a silk screen made of decoration. Today we introduce the aperture and wire diameter of the decorative hook mesh.

The bonding and anchoring function between the cold rolled ribbed steel bar and concrete is outstanding. In reinforced concrete structure, the width of black iron wire processing crack is smaller than that of circular steel bar, even than that of hot rolled thread steel bar. Therefore, it is used in the component, which fundamentally eliminates the phenomenon of steel wire sliding and damage, and improves the load bearing ability and crack resistance ability of the component end.

Under any application environment, users hope that the welding mesh has better strength, as long as it has improved in strength, it will make better use of the demand, but to make the strength of this product improve, also need to have many conditions, to see what kind of data manufacturers have in production, the strength of the product is the strength of the data, But a manufacturer does not meet the strength requirements in the data, and naturally, it cannot make the strength of the product improve after all, so this is the condition.

The distance between the adjacent two thorn rope installation do not know whether you have noticed? Careful observation can find that its spacing is not the same, the thorn rope factory for customer consultation when asking the installation height of the reason.

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.

Cold galvanizing is also called electric galvanizing. It is the use of electrolytic equipment to remove oil, pickling, and then put the pipe into the solution of zinc salt, and connect the anode of the electrolytic equipment, place zinc plate on the opposite side of the pipe, and connect the positive pole of the electrolytic equipment to the power supply. A layer of zinc is deposited on the pipe fitting by directional movement of an electric current from the positive pole to the negative pole. Cold plated pipe fitting is processed before galvanizing.

Welding electrode has a wide range of applications, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding.

Industrial rust prevention method: coated with asphalt, iron roof, coated with asphalt, you can prevent rust. Metal coating: Some metal surface will form a dense oxide film, can be coated on the surface of the metal composed of this metal screen. Such as: galvanized iron, tinplate plating, bicycle underwire and some medical equipment are coated with chromium and nickel.