Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.

5, according to the wire diameter thickness to adjust zinc dipping time

We basically know that the barbed wire fence generally has two kinds of ring and linear filamentous, the overall protective wire mesh selection of galvanized, stainless steel processing raw materials, long-term use is not easy to rust. Barbed wire fence uses stainless steel barbed wire, plastic coated barbed wire, aluminum coated barbed wire, galvanized barbed wire and other raw materials through special wire drawing into the strand planning, has a strong role in protection and maintenance. Widely used on both sides of the highway, grassland, gardens and other places, because it is a field protection product and therefore updated faster, so how to use the barbed wire fence after abandonment? Here are some of the uses of discarded blades.

Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.