Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.

Some customers pay more attention to the quality problem, so they pay more attention to the service life. The barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

Large rolls of galvanized silk play a very important role in our life. Made of low carbon steel rod processing, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.

Generally, the main reasons for the rust of iron wire are: when the steel mesh in the metal mesh appears some dust, this time you can use some water or alkaline solution cleaning. Followed by floating iron or embedded iron, iron will rust, connected to the stainless steel plate mesh of iron rust, so these iron must be dealt with, can use carbon steel wire brush can also be used for processing carbon steel and so on. Then is the scratch, for the scratch, mainly in the production process, need some stubborn iron scratch stainless steel plate net special polishing cleaning machine.

The main difference between the two is the carbon content. The carbon content of iron is 2.11 percent or greater, while the carbon content of steel is 2.11 percent or less. The iron carbon alloy with carbon content above 2.11% is cast iron (pig iron), which is basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different. The content of harmful impurities such as sulfur and phosphorus in steel is smaller. Steel wire general color focus, iron wire color light point, white point.

The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.